Courtesy of The Dental Advisor: 

The Dental Advisor Report header

Description

Tetric EvoCeram is a universal, hybrid composite indicated for anterior and posterior esthetic restorations. The composite is radiopaque and formulated to meet any rigorous esthetic challenge with availability in Enamel, Dentin, and bleach shades. This light-cured composite consists of particles ranging in size from 40 to 3000 nm with an average particle size of about 550 nm. It is packed in 0.2 g, color-coded, unit-dose capsules and 3 g color-coded syringes.

Figure 1Clinical Evaluation Protocol

  • 873 restorations were placed and monitored over an eight-year period.
  • 637 (73%) of these restorations were recalled over a six-month period. The restorations included both anterior and posterior teeth (Figure 1).
  • The recalled restorations were Class I, Class II, and Class IV composites (Figure 2).
  • Timeline of restorations in clinical service is shown in Figure 3.
  • At recall the following categories, esthetics, resistance to fracture/chipping, resistance to marginal discoloration, and wear resistance were rated on a scale of 1 to 5 with 1=poor, 2=fair, 3=good, 4=very good, 5=excellent. Any restoration receiving a rating of 1 or a 2 in a category is automatically replaced. Restorations receiving a rating of 3 or 4 in a category are still clinically acceptable and are not replaced.

Figure 2 and 3

Clinical Observations

Esthetics

The esthetics of Tetric EvoCeram was excellent at recall (Figure 4). Out of 637 recalled restorations, 93% received an excellent rating and 7% received good to very good rating and did not require replacement. Only three restorations (0.5%) required replacement because of poor esthetics. Tetric EvoCeram layered with a translucent shade often resulted in improved esthetics, opalescence and translucency. Layering is especially important in teeth that are discolored

Resistance to Fracture and Chipping 

Figure 4Over 95% of the 637 recalled Tetric EvoCeram restorations received an excellent rating (Figure 4). 2% of the restorations had chipped but did not require replacement, while 3% or 19 restorations did need to be replaced. Tetric EvoCeram proved to be very resistant to fracture and chipping at 8 years, especially given that 96% of the restorations were posterior restorations and were subjected to high occlusal forces.

Resistance to Marginal Discoloration 

Microleakage is affected by both the composite and the bonding agent. Excessive microleakage can lead to decay or poor marginal esthetics. 86% of the recalled restorations had no visible micro leakage and were rated excellent (Figure 4). 13% had slight to medium microleakage, while 1% had excessive microleakage which necessitated the replacement of the restoration. A variety of self-etch (88%) and total-etch (12%) bonding agents were used.

Wear Resistance

98% of the restorations showed no evidence of wear and received an excellent rating, whereas 1.5% of the restorations received a good or very good rating (Figure 4). Only 0.5% of the restorations required replacement because of excessive wear.

Conclusions

Tetric EvoCeram has excellent handling characteristic. It is non-slumping, not sticky, contours well, and is easy to finish and polish. This eight-year evaluation of 637 restorations demonstrated that Tetric EvoCeram had superior performance in esthetics, resistance to fracture/chipping, resistance to marginal discoloration, and wear resistance. Tetric EvoCeram received a 97% clinical performance rating.

Ask Dr. Johnson 8yr rpt